CCT-1

This is an accelerated laboratory corrosion test method that can be used to determine the corrosion resistance of automotive assemblies and components. It is cyclic in nature, i.e.; test specimens are exposed to changing climates over time.

Test specimens are placed in an enclosed chamber and exposed to a changing climate that comprises of the following 3 part repeating cycle. 4.0 hours exposure to a continuous indirect spray of neutral (pH 6.5 to 7.2) salt water solution, which falls-out on to the specimens at a rate of 1.0 to 2.0ml/80cm²/hour, in a chamber temperature of +35C . This is followed by 2.0 hours of air drying in a climate of 20 to 30%RH at +60C. This is followed by 2.0 hours exposure to a condensing water climate (wetting) of 95 to 100%RH at +50C. The number of cycle repeats and therefore the test duration is variable.

The maximum transition times between each part of the test cycle are also specified as follows:

• From salt spraying to air drying within 30 minutes.
• From air drying to wetting within 15 minutes.
• From wetting to salt spraying within 30 minutes.